Process for manufacturing a power semiconductor device having charge-balance columnar structures on a non-planar surface, and corresponding power semiconductor device

ABSTRACT

An embodiment of a process for manufacturing a power semiconductor device envisages the steps of: providing a body of semiconductor material having a top surface and having a first conductivity; forming columnar regions having a second type of conductivity within the body of semiconductor material, and surface extensions of the columnar regions above the top surface; and forming doped regions having the second type of conductivity, in the proximity of the top surface and in contact with the columnar regions. The doped regions are formed at least partially within the surface extensions of the columnar regions; the surface extensions and the doped regions have a non-planar surface pattern, in particular with a substantially V-shaped groove.

PRIORITY

The present application is a Divisional of U.S. patent application Ser.No. 12/298,025; which application claims benefit pursuant to 35 USC §371of PCT Patent Application Ser. No. PCT/IT2006/000273, published inEnglish, filed Apr. 21, 2006, which these applications are incorporatedherein by reference in their entirety.

Cross Reference to Related Applications

This application is related to U.S. patent application Ser. No.12/296,921, filed Oct. 10, 2008, entitled PROCESS FOR MANUFACTURING ASEMICONDUCTOR POWER DEVICE COMPRISING CHARGE-BALANCE COLUMN STRUCTURESAND RESPECTIVE DEVICE, which is incorporated herein by reference in itsentirety.

TECHNICAL FIELD

An embodiment of the present disclosure relates to a process formanufacturing a power semiconductor device having charge-balancecolumnar structures on a non-planar surface, and to a correspondingpower semiconductor device. In particular, the ensuing treatment willmake explicit reference, without this implying any loss of generality,to the manufacturing of a power MOS device.

BACKGROUND

In the last few years a wide range of solutions have been developed inorder to increase the efficiency of power semiconductor devices, inparticular in terms of increase in the breakdown voltage and decrease inthe output resistance.

For example, U.S. Pat. Nos. 6,586,798, 6,228,719, 6,300,171 and6,404,010, all commonly owned and incorporated by reference, describevertical-conduction power semiconductor devices, wherein, within anepitaxial layer forming part of a drain region having a givenconductivity type, columnar structures of opposite conductivity areformed. These columnar structures have a dopant concentration equal andopposite to the dopant concentration of the epitaxial layer, so as toenable a substantial charge balance (the so-called multi-drain or MDtechnology). The charge balance enables high breakdown voltages to beobtained, and, in addition, the high dopant concentration of theepitaxial layer enables a low output resistance (and hence low losses inconduction) to be obtained. The use of MD technology has enabled theso-called “ideal limit of silicon” to be overcome.

In summary, the formation of the aforesaid columnar structures envisagesa sequence of steps of growth of N-type epitaxial layers, each stepbeing followed by a step of implantation of a P-type dopant. Theimplanted regions are stacked so as to form the columnar structures.Next, body regions of the power device are formed in contact with thecolumnar structures, so that the columnar structures constitute anextension of the body regions within the drain region.

The evolution of said technology has witnessed a progressive increase inthe density of the elementary strips forming the devices in order tofurther increase the concentration of charge of the epitaxial layer andto obtain devices which, given the same breakdown voltage (which issubstantially related to the height of the columnar structures), have alower output resistance. On the other hand, however, the increase in thedensity of the elementary strips entails a corresponding increase in thenumber of the steps of epitaxial growth and a reduction in the thermalbudget of the devices, and consequently an increase in the manufacturingcosts and times, and in the defectiveness intrinsically linked to thesteps of epitaxial growth.

Alternative technologies have consequently been developed to obtain thecharge-balance columnar structures, said technologies envisaging, forexample, formation of trenches within the epitaxial layer and subsequentfilling of said trenches with semiconductor material appropriately dopedto obtain the charge balance.

For example, solutions are known according to which the trenches arefilled via steps of epitaxial growth of semiconductor material (see forexample U.S. Pat. No. 6,495,294, US 2003224588 and US 2003219933 whichare incorporated by reference), possibly alternated by steps of etchingof surface-growth portions. In particular, a non-selective epitaxialgrowth also involves a top surface of the layer in which the trenchesare provided, and at the end of the epitaxial process a wrinkled surfacelayer of semiconductor material is consequently formed, characterized bythe presence of a plurality of grooves in areas corresponding to thecolumnar structures. The known techniques envisage removal of thewrinkled surface layer via the CMP (Chemical-Mechanical Polishing)technique in order to planarize the top surface prior to formation ofbody, gate and source structures of the power devices.

As a whole, the solutions described for obtaining power devices withcharge-balance structures may not be satisfactory, either as regards thecomplexity and costs of their manufacturing and as regards attainment ofa real charge balance (for example, due to a poor uniformity of thespatial charge distribution or due to the presence of residual defects).

SUMMARY

An embodiment of the present disclosure is a process for manufacturing acharge-balance power device that enables the aforesaid problems anddisadvantages to be overcome, and that is simple and inexpensive tocarry out.

BRIEF DESCRIPTION OF THE DRAWINGS

For a better understanding of the concepts described herein, embodimentsare now described, purely by way of non-limiting example and withreference to the attached drawings, wherein:

FIGS. 1 to 8 show cross sections through a wafer of semiconductormaterial regarding successive steps of a manufacturing process accordingto a first embodiment of the present disclosure;

FIGS. 9 and 10 show possible variants of the first embodiment of thepresent disclosure;

FIGS. 11 to 17 show cross sections through a wafer of semiconductormaterial regarding successive steps of a manufacturing process accordingto a second embodiment of the present disclosure; and

FIGS. 18 and 19 show possible variants of the second embodiment of thepresent disclosure.

DETAILED DESCRIPTION

FIG. 1 shows a wafer 1 of semiconductor material, typically silicon,comprising a substrate 2 having a first type of conductivity, forexample, an N⁺⁺ type with resistivity of less than approximately 10Ω·cm, and an epitaxial layer 3, which also has the first type ofconductivity, for example, an N type with a resistivity of approximatelybetween 0.1 Ω·cm and 2 Ω·cm. The wafer 1 has, for example, a surfaceorientation <100>, and the epitaxial layer 3 has a top surface 4. Overthe entire wafer an implantation of an N type with low energy(approximately 50-100 keV) and dosage of approximately between 10¹¹ and10¹³ at/cm² is carried out, without masking, in order to form asurface-implant layer 5 in the proximity of the top surface 4 of theepitaxial layer 3.

Next (FIG. 2), within the epitaxial layer 3 a plurality of columnarstructures 6 for charge balance is formed. As has been described indetail in the copending patent application PCT/IT2006/000244 filed onApr. 11, 2006, the process for forming the columnar structures 6envisages in the first place formation, by means of anisotropic dryetching through a purposely provided masking, of deep trenches 8 withinthe epitaxial layer 3 (and hence through the surface-implant layer 5),having for example a width, at the level of the top surface 4, ofapproximately between 0.8 and 2 μm and a smaller width on the bottom ofapproximately between 0.2 and 1.4 μm. In addition, the height of thedeep trenches 8 ranges, for example, from approximately 5 to 50 μm anddetermines, together with the thickness of the epitaxial layer 3, thevoltage class of the final device (for example, a voltage class of 100 Vcorresponds to a height of 5 μm, whereas a voltage class of 600 Vcorresponds to a height of 30 μm). The cut-off voltage of the resultingdevice can range approximately between 100 and 1500 V, according to thethickness of the epitaxial layer 3. Then, the wafer 1 is subjected to anannealing treatment in a hydrogen environment at a temperature ofapproximately 1000-1150° C. for a treatment time of approximately 1 to15 min. Said treatment, in addition to removing the damage due to theprevious dry etch, leads to exposure, on the bottom of the deep trenches8, of the crystallographic planes <100> and <130> and, along the sidewalls, of the plane <010> (the deep trenches 8 consequently assume theshape visible in FIG. 2). Next, the deep trenches 8 are filled viaepitaxial growth with silicon doped with a second conductivity type, inthe example, the P type (for instance, doped with boron ions). Inparticular, the epitaxial growth occurs by supplying flows of a gascontaining silicon (for example, dichlorosilane) and of a gas containingboron (for example, diborane), and control of doping is ensuredmaintaining an approximately constant gradient of growth in the flow ofdiborane (for example, setting a linear ramp increasing from an initialflow value to a final flow value twice the initial one), and maintainingthe flow of dichlorosilane approximately constant. Given that the growthis not selective with respect to the deep trenches 8, the epitaxialgrowth occurs both within the trenches starting from the side walls, ata higher rate in the proximity of the surface, and on the outside of thetrenches, in particular on the top surface 4 of the epitaxial layer 3.In order to prevent premature closing of the deep trenches 8 due to theencounter of the fronts of growth from the walls, successive steps ofepitaxial growth are consequently alternated with etching steps, forexample with HCl, of the surface-growth portions (the so-calledmulti-step process). At the end of said process sequence, the structureshown in FIG. 2 is obtained, with formation of the columnar structures6, filling the deep trenches 8 substantially completely and having asubstantially uniform spatial distribution of dopant and reducedpresence of defects (for example voids). The process of non-selectiveepitaxial growth involves also the top surface 4 of the epitaxial layer3, over which a wrinkled surface layer 9 of a P type is formed, withgrooves in areas corresponding to the columnar structures 6. Inparticular, each columnar structure 6 has thus a surface extension 10,at and over the top surface 4, having a non-planar surface pattern and acharacteristic grooved, in particular V-shaped, cross section.Connection portions 11 of the wrinkled surface layer 9, having a planarsurface pattern, connect the surface extensions 10 of adjacent columnarstructures 6. In addition, said adjacent columnar structures 6 areseparated, at the top surface 4, by respective implant portions 5 a ofthe implant layer 5.

The subsequent figures show for greater clarity an enlargement of asurface portion of the wafer 1, shown by a dashed rectangle in FIG. 2,which encloses a pair of adjacent columnar structures 6 (in practice,two strips of the device). It is clear, however, that the process stepsdescribed hereinafter regard also the remaining part of the device.

As will be clarified hereinafter, an embodiment of the presentdisclosure envisages providing a power device on a non-planar surfacepartially within the wrinkled surface layer 9, exploiting portions ofsaid layer, in particular the surface extensions 10 of the columnarstructures 6, as active areas of the device. In other words, the processaccording to an embodiment of the disclosure does not envisage apreventive step of planarization of the wafer surface (for example viaCMP), with advantages in terms of costs and simplicity of manufacturing.

In detail (FIG. 3), in a surface region of the connection portions 11,implants of an N type are performed, through a purposely provided mask,for example, with medium energy (approximately 80-160 keV) and a dosageof approximately between 5·10¹¹ and 10¹³ at/cm², in order to formsurface contact regions 12.

Then (FIG. 4), a process of thermal diffusion is performed to providesinkers 14 of an N type, which reverse the conductivity of therespective connection portions 11 and reach the underlying implantportions 5 a, which are also of an N type. The diffusion process canpossibly be omitted when the conditions of the prior implant (in termsof dosage and energy) and the thickness of the wrinkled surface layer 9enable formation of the sinkers 14 even in the absence of said process.It should be noted in any case that the sinkers 14 separate adjacentsurface extensions 10, enabling, as will be described in detailhereinafter, formation of devices having a cell structure.

Next, a gate oxide layer 15 (made of thermal oxide), of a thickness ofapproximately between 20 nm and 150 nm, is grown over the wafer 1 in theactive area, and a polysilicon layer 16, having a thickness ofapproximately between 200 nm and 700 nm, is then formed over the gateoxide layer 15. The polysilicon layer 16 is etched via selective dryetching through a purposely provided mask so as to obtain gate regions18 above the sinkers 14 (FIG. 5).

Next (FIG. 6), through the gate oxide layer 15 and exploiting the gateregions 18 as hard masks, a body implant is carried out, for example,with boron atoms and an implant dosage of approximately between 10¹³ and10¹⁴ at/cm² and an energy of approximately between 80 and 200 keV(chosen as a function of the thickness of the gate regions 18), followedby a thermal process of diffusion to form body regions 19. Inparticular, the body regions 19 are formed within the surface extensions10 of the columnar structures 6, consequently reproducing the non-planarpattern with grooved cross section, and partially within the sinkers 14underneath the gate regions 18 (where they form channel regions of thepower device).

Next, through a purposely provided masking (not illustrated) alignedwith the mask that has defined the gate regions 18, a deep-bodyimplantation of a P⁺⁺ type is carried out using boron ions with animplantation dosage of approximately between 5·10¹⁴ and 5·10¹⁵ at/cm²and an energy of approximately between 80 and 300 keV. There follows athermal process of diffusion to form deep-body regions 20 in a centralarea of the surface extensions 10 (FIG. 7).

Next (FIG. 8), through a purposely provided masking, a sourceimplantation of an N⁺ type is carried out, for example with atoms ofphosphorus P or arsenic As with an implantation dosage of approximatelybetween 5·10¹⁴ and 5·10¹⁵ at/cm² and an energy of approximately between60 and 200 keV, to form first and second source regions 22 a, 22 bwithin the body regions 19 and deep-body regions 20. In particular, thefirst source regions 22 a occupy surface portions of body regions offirst columnar structures 6 a entirely, whilst the second source regions22 b are arranged in outer surface portions of body regions of secondcolumnar structures 6 b, which alternate with the first columnarstructures 6 a within the epitaxial layer 3 (so as to obtainsubsequently, for known reasons, a short circuit between the source andbody regions of the power device).

Next, a process of deposition of an intermediate dielectric layer 23with a thickness of approximately between 500 nm and 1 μm is carriedout, as well as a thermal activation process. Then contacts are opened,by means of masking and subsequent etching of the intermediatedielectric layer 23 and gate oxide layer 15; said etching being entirelydry, or wet for a first part and dry for a second part. Next, forexample by means of a sputtering process, metallization of the front ofthe wafer 1 is performed, with formation of a metal layer 24, thethickness of which depends upon the capacity to sustain current to beguaranteed for the device.

The process ends with final steps of a known type, including etching ofthe metal layer 24, deposition of a passivation layer and a subsequentstep of masking and etching of the passivation layer, and a process offinishing of the back.

At the end of the manufacturing process, a power MOS device 25 isobtained on a non-planar surface, with the oxide and the gate region inthe planar area, and the body region in the non-planar area (inparticular within the surface extension of a charge-balance columnarstructure).

FIG. 9 shows a variant of the structure of FIG. 8, in which the columnarstructures 6 extend throughout the thickness of the epitaxial layer 3and terminate at the bottom within the substrate 2.

FIG. 10 shows a further variant of the structure of FIG. 8, in which abuffer layer 26, of an N type, extends between the substrate 2 and theepitaxial layer 3. In this case, the columnar structures 6 terminateinside the buffer layer 26. In particular, the presence of the bufferlayer 26 enables a greater control over the dopant concentration in theproximity of the bottom of the columnar structures 6 to be achieved, andconsequently also control of concentrations of electric field that couldlead to phenomena of breakdown of the device.

A second embodiment of the present disclosure is now described, withreference to FIGS. 11-17, in which elements corresponding to the onespreviously described are designated by the same reference numbers.

In detail, in an initial step of the manufacturing process, thecharge-balance columnar structures 6 are formed in the epitaxial layer 3overlying the substrate 2, in a way altogether similar to what has beendescribed previously. At the end of said step, the wrinkled surfacelayer 9 is formed on the top surface 4 of the epitaxial layer 3, saidwrinkled surface layer 9 comprising the surface extensions 10 of thecolumnar structures 6 and the connection portions 11 having asubstantially planar pattern (FIG. 11).

Once again, the subsequent figures show, for reasons of greater clarity,an enlargement of a surface portion of the wafer 1, shown by a dashedrectangle in FIG. 11, which encloses a pair of adjacent columnarstructures 6.

Then, over the surface of the wafer 1 an implantation of a P type iscarried out, without masking, for example using boron with animplantation dosage of approximately between 10¹³ and 10¹⁴ at/cm² and anenergy of approximately between 80 and 200 keV, to form a body layer 30(FIG. 12). Possibly, the implantation can be carried out through asacrificial oxide of appropriate thickness (ion pre-implantation oxide)and be followed by a purposely provided process of diffusion. The bodylayer 30 extends within the wrinkled surface layer 9, and in particularat the surface extensions 10 of the columnar structures 6.

Next (FIG. 13), over the surface of the wafer 1, once again withoutmasking, a blanket implantation of an N type is carried out, for exampleusing phosphorus or arsenic with an implantation dosage of between5·10¹⁴ and 5·10¹⁵ at/cm² and an energy of between 60 and 200 keV, toform a source layer 32 in a surface portion of the wafer 1.

Through a purposely provided mask, two successive implantations of a Ptype are then carried out (FIG. 14): a first surface implantation forenriching contact with the region of a P type, with a dosage ofapproximately between 10¹⁴ and 10¹⁵ at/cm² and an energy ofapproximately between 30 and 100 keV; and a second deep implantation toobtain deep-body regions, designated once again by 20, with a dosage ofapproximately between 5·10¹⁴ and 5·10¹⁵ at/cm² and an energy ofapproximately between 80 and 300 keV. In particular, the deep-bodyregions 20 are formed in positions corresponding to the surfaceextensions of first columnar structures 6 a, and not in second columnarstructures 6 b that alternate with the first columnar structures 6 awithin the epitaxial layer 3.

Next (FIG. 15), at the connection portions 11 of the wrinkled surfacelayer 9, surface trenches 34 are opened, which traverse said connectionportions 11 and reach the underlying epitaxial layer 3. The surfacetrenches 34 also define body regions 19 of the power device. It shouldbe noted that the surface trenches 34 separate adjacent surfaceextensions 10.

In the active area a gate oxide layer 15 (thermal oxide) of a thicknessof between 20 nm and 150 nm is then deposited over the wafer 1, and ontop of it a polysilicon layer 16, of a conformable type, is deposited.In particular, the polysilicon layer 16 fills the surface trenches 34previously formed (FIG. 16).

The polysilicon layer 16 is then etched by means of selective dryetching and a purposely provided masking so as to obtain gate regions 18at the surface trenches 34 (FIG. 17). There follows the deposition of anintermediate dielectric layer 23 with a thickness of approximatelybetween 500 nm and 1 μm. Then contacts are opened, by means of maskingand subsequent etching of the intermediate dielectric layer 23 and ofthe gate oxide layer 15; said etching being entirely dry or wet in afirst part and dry in a second part. A sputtering process leads to themetallization of the front of the wafer 1, with formation of a metallayer 24, the thickness of which depends upon the capacity to sustaincurrent to be guaranteed for the device. The process terminates withfinal steps of a known type, in a way altogether similar to the onedescribed previously.

At the end of the manufacturing process according to the secondembodiment, a power MOS device 35 is consequently obtained on a non-planar surface, with the oxide and the channel region in an area definedby a trench-formation process. In particular, the channel region extendsvertically within the body layer 30 between the source layer 32 and theepitaxial layer 3, at the sides of the trenches 34. Once again, the bodyregion is in the non-planar area, within the surface extension of acharge-balance columnar structure.

FIGS. 18 and 19 show variants of the structure of FIG. 16, in which thecolumnar structures 6 extend until the substrate 2 and a buffer layer26, of an N type, arranged between the substrate 2 and the epitaxiallayer 3 are, respectively, reached.

Advantages of the manufacturing process and of the corresponding powerdevice are evident from the above description.

In any case, it is emphasized once again that the processes describedenables charge-balance power devices to be obtained without resorting toa preventive step of planarization of the surface of the wafer ofsemiconductor material after the formation of the charge-balancecolumnar structures. The resulting power device has a cell structurewith high-density strips, and is formed on a non-planar surface, withbody regions within the surface extensions of the columnar structuresthat are formed in the process of non-selective epitaxial filling.

In particular, power MOS devices may be obtained with the channel andthe gate structure formed in a planar area (first embodiment), or elsein an area obtained by means of processes of trench formation (secondembodiment).

Thanks to charge balance, it is possible to achieve values ofresistivity of the epitaxial layer of less than approximately 2 Ω·cm,and values of cut-off voltage of approximately between 100 and 1500 V asa function of the thickness of the epitaxial region.

It is clear that modifications and variations can be made to what isdescribed and illustrated herein, without thereby departing from thescope of the disclosure.

In particular, by applying the concepts described, it is possible toprovide different power devices, for example an IGBT (Insulated-GateBipolar Transistor), a bipolar diode, or a Schottky diode.

Furthermore, the possibility of providing dual structures is evident, inwhich charge balance is obtained by formation of columnar structureswith an N doping in an epitaxial layer having a P doping.

Moreover, a system such as an automobile may include first integratedcircuit that includes a described power device, and included a secondintegrated circuit, such as a controller, coupled to the firstintegrated circuit.

1-13. (canceled)
 14. A power semiconductor device, comprising: a body ofsemiconductor material having a first type of conductivity; columnarregions having a second type of conductivity, arranged within said bodyof semiconductor material; and doped regions having said second type ofconductivity, arranged in the proximity of a surface portion of saidbody of semiconductor material and in contact with said columnarregions, wherein said doped regions having have a non-planar surfacepattern.
 15. The device according to claim 14, wherein said dopedregions have a grooved, in particular substantially V-shaped, surfacepattern.
 16. The device according to claim 14, wherein said powersemiconductor device is a MOS device, and said doped regions comprisebody regions; said device further comprising gate structures arrangedbetween adjacent columnar regions, at least in part above said body ofsemiconductor material, and source regions having said first type ofconductivity, arranged within said body regions; said columnar regionshaving a doping level such as to substantially balance a doping level ofan opposite type of said body of semiconductor material.
 17. The deviceaccording to claim 16, wherein said gate structures comprise arespective insulating region arranged above a substantially planarportion of said body of semiconductor material between adjacent bodyregions, and a respective conductive region arranged on said insulatingregion; said insulating regions and said conductive regions having asubstantially planar surface pattern.
 18. The device according to claim16, wherein said gate structures comprise a respective insulating regionand a respective conductive region extending in part through said bodyof semiconductor material laterally in contact with adjacent bodyregions.
 19. The device according to claim 14, further comprising asubstrate; wherein said body of semiconductor material comprises anepitaxial layer arranged on said substrate, and said columnar structuresextend through said epitaxial layer until said substrate is reached. 20.The device according to claim 14, further comprising a substrate and abuffer layer having said first type of conductivity on said substrate;wherein said body of semiconductor material comprises an epitaxial layerarranged on said buffer layer, and said columnar structures extendthrough said epitaxial layer until said buffer layer is reached.
 21. Atransistor, comprising: a first semiconductor layer of a firstconductivity, at least a portion of the first semiconductor layerincluding a drain region; a first trench disposed in the firstsemiconductor layer; a first filler of a second conductivity disposed inthe first trench; a first body region of the second conductivitydisposed over and in contact with the first filler and having at leastone sloped side; and a first source region of the first conductivitydisposed over and in contact with the first body region.
 22. Thetransistor of claim 21 wherein the body region has two sloped sides thatdefine a trough.
 23. The transistor of claim 21 wherein the body regionhas two sloped sides that define a substantially triangular trough. 24.The transistor of claim 21, further comprising: a second semiconductorlayer of the first conductivity disposed over the first semiconductorlayer and in contact with the first semiconductor layer and the bodyregion; and a gate disposed over the second semiconductor layer and overa portion of the body region adjacent to the second semiconductor layer.25. The transistor of claim 21, further comprising: a secondsemiconductor layer of the first conductivity disposed over the firstsemiconductor layer and in contact with the first semiconductor layerand the body region; a second trench disposed in the secondsemiconductor layer and contiguous with the body region; and a gatedisposed in the second trench.
 26. The transistor of claim 21, furthercomprising: a second semiconductor layer of the first conductivitydisposed over the first semiconductor layer and in contact with thefirst semiconductor layer and the body region; a second trench disposedin the second semiconductor layer, extending into the firstsemiconductor layer, and contiguous with the body region; and a gatedisposed in the second trench.
 27. The transistor of claim 21, furthercomprising: a second semiconductor layer over which the firstsemiconductor layer is disposed; and wherein the first trench and fillerextend into the second semiconductor layer.
 28. The transistor of claim21, further comprising a source conductor in contact with the sourceregion and isolated from the body region.
 29. The transistor of claim21, further comprising a source conductor in contact with the source andbody regions.
 30. The transistor of claim 21, further comprising: asecond trench disposed in the first semiconductor layer; a second fillerof the second conductivity disposed in the first trench; a second bodyregion of the second conductivity disposed over and in contact with thesecond filler and having at least one sloped side; and a second sourceregion of the first conductivity disposed over and in contact with thesecond body region.
 31. A device, comprising: a first semiconductorlayer of a first conductivity, at least a portion of the firstsemiconductor layer comprising a drain region; a plurality of trenchesdisposed in the first semiconductor layer; a plurality of filler regionsof a second conductivity respectively disposed in each of the pluralityof trenches; at least one body region of the second conductivitydisposed over and in contact with at least one filler region and havingat least one sloped side; and at least one source region of the firstconductivity disposed over and in contact with the at least one bodyregion.
 32. The device of claim 31, further comprising: a secondsemiconductor layer of the first conductivity disposed over the firstsemiconductor layer and in contact with the first semiconductor layerand the at least one body region; and at least one gate disposed overthe second semiconductor layer and over a portion of the at least onebody region adjacent to the second semiconductor layer.
 33. The deviceof claim 31, wherein, the at least one body region and the at least onesource region form a non-planar surface of the device.
 34. A transistor,comprising: a first semiconductor layer of a first conductivity, atleast a portion of the first semiconductor layer including a drainregion; a first trench disposed in the first semiconductor layer; afirst filler of a second conductivity disposed in the first trench; afirst body region of the second conductivity disposed over and incontact with the first filler and having at least one sloped side; afirst source region of the first conductivity disposed over and incontact with the body region; a second trench disposed in the firstsemiconductor layer; a second filler of a second conductivity disposedin the second trench; a second body region of the second conductivitydisposed over and in contact with the second filler and having at leastone sloped side; a second source region of the first conductivitydisposed over and in contact with the second body region.